Attributes
Technology | Polyurethane |
---|---|
Skin Time (23C/50%RH) | Approx. 60 mins |
Movement Capability | ± 25% |
Tensile Strength | approx. 1.5 N/mm2 |
Shore A Hardness | approx. 30 |
Curing rate (23C/50%RH) | approx.2.0mm/24h |
Attributes
Technology | Water based Acrylic |
---|---|
Skin Time (23C/50%RH) | approx. 30mins |
Movement Capability | ± 15% |
Tensile Strength | approx. 0.75 Mpa |
Shore A Hardness | N/A |
Curing rate (23C/50%RH) | N/A |
Attributes
Technology | Polyurethane |
---|---|
Skin Time (23C/50%RH) | approx. 30mins |
Movement Capability | ± 25% |
Tensile Strength | >1.8N/mm2 |
Shore A Hardness | approx. 40 -45 |
Curing rate (23C/50%RH) | ≥ 2,5 mm/24h |
Attributes
Technology | PSA composite |
---|---|
Skin Time (23C/50%RH) | |
Movement Capability | ± 25% |
Tensile Strength | |
Shore A Hardness | |
Curing rate (23C/50%RH) |
Attributes
Technology | Moisture curing silyl-modified polymer (SMP) |
---|---|
Skin Time (23C/50%RH) | Approx. 50 mins |
Movement Capability | ± 20% |
Tensile Strength | 1.1MPa |
Shore A Hardness | 31 |
Curing rate (23C/50%RH) |
Attributes
Technology | Moisture curing silyl-modified polymer (SMP) |
---|---|
Skin Time (23C/50%RH) | Approx. 50 mins |
Movement Capability | ± 20% |
Tensile Strength | 1.1MPa |
Shore A Hardness | 31 |
Curing rate (23C/50%RH) | 2 –3mm per day |
Attributes
Technology | Polyurethane |
---|---|
Skin Time (23C/50%RH) | approx. 35mins |
Movement Capability | ± 25% |
Tensile Strength | 1.5 –2.0 N/mm2 |
Shore A Hardness | Approx. 35 -40 |
Curing rate (23C/50%RH) | ≥ 2,5 mm/24h |
Attributes
Technology | Polyurethane |
---|---|
Skin Time (23C/50%RH) | approx. 25mins |
Movement Capability | ± 25% |
Tensile Strength | 2.0–2.5N/mm2 |
Shore A Hardness | 40±5 |
Curing rate (23C/50%RH) | Min. 3mm/24h |
Attributes
Technology | Moisture curing silyl-modified polymer (SMP) |
---|---|
Skin Time (23C/50%RH) | >2hours |
Movement Capability | ± 25% |
Tensile Strength | 1.0±0.2MPa |
Shore A Hardness | 22±5 |
Curing rate (23C/50%RH) | ~2.5mm/24hrs |
Attributes
Technology | Sil-X ™ |
---|---|
Skin Time (23C/50%RH) | Approx 40 minutes |
Movement Capability | N/A |
Tensile Strength | N/A |
Shore A Hardness | |
Curing rate (23C/50%RH) | Approx 3mm/24 hours |
Attributes
Technology | Acetic cure silicone |
---|---|
Skin Time (23C/50%RH) | 5 minutes |
Movement Capability | N/A |
Tensile Strength | N/A |
Shore A Hardness | 23 |
Curing rate (23C/50%RH) | 3mm/24 hours |
Attributes
Technology | Neutral (oxime) cure silicone |
---|---|
Skin Time (23C/50%RH) | 5–10 minutes |
Movement Capability | ± 25% |
Tensile Strength | 2.0 Mpa |
Shore A Hardness | 28 |
Curing rate (23C/50%RH) | 10mm in 5–7 days |
Attributes
Technology | Neutral (oxime) cure silicone |
---|---|
Skin Time (23C/50%RH) | 4–8 minutes |
Movement Capability | ± 25% |
Tensile Strength | 2.0 Mpa |
Shore A Hardness | 28 |
Curing rate (23C/50%RH) | 10mm in 5–7 days |
Attributes
Technology | Neutral (oxime) cure silicone |
---|---|
Skin Time (23C/50%RH) | 4–8 minutes |
Movement Capability | ± 25% |
Tensile Strength | 2.0 Mpa |
Shore A Hardness | 28 |
Curing rate (23C/50%RH) | 10mm in 5–7 days |
Attributes
Technology | Neutral (oxime) cure silicone |
---|---|
Skin Time (23C/50%RH) | 5–10 minutes |
Movement Capability | ± 25% |
Tensile Strength | 2.0 MPa (clear) 1.3 MPa (black) |
Shore A Hardness | 28 (clear) 30 (black) |
Curing rate (23C/50%RH) | 10mm in 5–7 days |
Attributes
Technology | Alkyl Resin |
---|---|
Skin Time (23C/50%RH) | N/A |
Movement Capability | ± 5% |
Tensile Strength | N/A |
Shore A Hardness | N/A |
Curing rate (23C/50%RH) | N/A |
Attributes
Technology | Polybutene |
---|---|
Skin Time (23C/50%RH) | N/A |
Movement Capability | ± 8% |
Tensile Strength | N/A |
Shore A Hardness | N/A |
Curing rate (23C/50%RH) | N/A |
Attributes
Technology | Advanced Hybrid Technology |
---|---|
Skin Time (23C/50%RH) | 45-55 mins |
Movement Capability | +/-15% |
Tensile Strength | |
Shore A Hardness | 30 +/-5 |
Curing rate (23C/50%RH) | ~3 mm/24h |