Compare

Attributes

Technology Polyurethane
Skin Time (23C/50%RH) approx. 25mins
Movement Capability ± 25%
Tensile Strength 2.0–2.5N/mm2
Shore A Hardness 40±5
Curing rate (23C/50%RH) Min. 3mm/24h

Attributes

Technology Water based Acrylic
Skin Time (23C/50%RH) approx. 30mins
Movement Capability ± 15%
Tensile Strength approx. 0.75 Mpa
Shore A Hardness N/A
Curing rate (23C/50%RH) N/A

Attributes

Technology Polyurethane
Skin Time (23C/50%RH) Approx. 60 mins
Movement Capability ± 25%
Tensile Strength approx. 1.5 N/mm2
Shore A Hardness approx. 30
Curing rate (23C/50%RH) approx.2.0mm/24h

Attributes

Technology Polyurethane
Skin Time (23C/50%RH) approx. 30mins
Movement Capability ± 25%
Tensile Strength >1.8N/mm2
Shore A Hardness approx. 40 -45
Curing rate (23C/50%RH) ≥ 2,5 mm/24h

Attributes

Technology PSA composite
Skin Time (23C/50%RH)
Movement Capability ± 25%
Tensile Strength
Shore A Hardness
Curing rate (23C/50%RH)

Attributes

Technology Moisture curing silyl-modified polymer (SMP)
Skin Time (23C/50%RH) Approx. 50 mins
Movement Capability ± 20%
Tensile Strength 1.1MPa
Shore A Hardness 31
Curing rate (23C/50%RH)

Attributes

Technology Moisture curing silyl-modified polymer (SMP)
Skin Time (23C/50%RH) Approx. 50 mins
Movement Capability ± 20%
Tensile Strength 1.1MPa
Shore A Hardness 31
Curing rate (23C/50%RH) 2 –3mm per day

Attributes

Technology Polyurethane
Skin Time (23C/50%RH) approx. 35mins
Movement Capability ± 25%
Tensile Strength 1.5 –2.0 N/mm2
Shore A Hardness Approx. 35 -40
Curing rate (23C/50%RH) ≥ 2,5 mm/24h

Attributes

Technology Moisture curing silyl-modified polymer (SMP)
Skin Time (23C/50%RH) >2hours
Movement Capability ± 25%
Tensile Strength 1.0±0.2MPa
Shore A Hardness 22±5
Curing rate (23C/50%RH) ~2.5mm/24hrs

Attributes

Technology Sil-X ™
Skin Time (23C/50%RH) Approx 40 minutes
Movement Capability N/A
Tensile Strength N/A
Shore A Hardness
Curing rate (23C/50%RH) Approx 3mm/24 hours

Attributes

Technology Moisture curing silyl-modified polymer (SMP)
Skin Time (23C/50%RH) 15 to 30 min
Movement Capability ± 20%
Tensile Strength Approx. 1.4 MPa
Shore A Hardness 40 ± 5
Curing rate (23C/50%RH) Approx 3.0mm/24 hr

Attributes

Technology Acetic cure silicone
Skin Time (23C/50%RH) 5 minutes
Movement Capability N/A
Tensile Strength N/A
Shore A Hardness 23
Curing rate (23C/50%RH) 3mm/24 hours

Attributes

Technology Neutral (oxime) cure silicone
Skin Time (23C/50%RH) 5–10 minutes
Movement Capability ± 25%
Tensile Strength 2.0 Mpa
Shore A Hardness 28
Curing rate (23C/50%RH) 10mm in 5–7 days

Attributes

Technology Neutral (oxime) cure silicone
Skin Time (23C/50%RH) 4–8 minutes
Movement Capability ± 25%
Tensile Strength 2.0 Mpa
Shore A Hardness 28
Curing rate (23C/50%RH) 10mm in 5–7 days

Attributes

Technology Neutral (oxime) cure silicone
Skin Time (23C/50%RH) 4–8 minutes
Movement Capability ± 25%
Tensile Strength 2.0 Mpa
Shore A Hardness 28
Curing rate (23C/50%RH) 10mm in 5–7 days

Attributes

Technology Neutral (oxime) cure silicone
Skin Time (23C/50%RH) 5–10 minutes
Movement Capability ± 25%
Tensile Strength 2.0 MPa (clear) 1.3 MPa (black)
Shore A Hardness 28 (clear) 30 (black)
Curing rate (23C/50%RH) 10mm in 5–7 days

Attributes

Technology Butyl rubber
Skin Time (23C/50%RH) N/A
Movement Capability ± 8%
Tensile Strength N/A
Shore A Hardness N/A
Curing rate (23C/50%RH) N/A

Attributes

Technology Alkyl Resin
Skin Time (23C/50%RH) N/A
Movement Capability ± 5%
Tensile Strength N/A
Shore A Hardness N/A
Curing rate (23C/50%RH) N/A

Attributes

Technology Polybutene
Skin Time (23C/50%RH) N/A
Movement Capability ± 8%
Tensile Strength N/A
Shore A Hardness N/A
Curing rate (23C/50%RH) N/A